Catalytic hydrodechlorination of trichloroethylene in water with supported CMC-stabilized palladium nanoparticles.

In this work, we developed and tested a new class of supported Pd catalysts by immobilizing CMC (carboxymethyl cellulose) stabilized Pd nanoparticles onto alumina support. The alumina supported Pd nanoparticles were able to facilitate rapid and complete hydrodechlorination of TCE (trichloroethylene) without intermediate by-products detected. With a Pd mass loading of 0.33 wt% of the alumina mass, the observed pseudo first order reaction rate constant, k(obs), for the catalyst was increased from 28 to 109 L/min/g when CMC concentration was raised from 0.005 to 0.15 wt%. The activity increase was in accord with an increase of the Pd dispersion (measured via CO chemisorption) from 30.4% to 45.1%. Compared to the commercial alumina supported Pd, which has a lower Pd dispersion of 21%, our CMC-stabilized Pd nanoparticles offered more than 7 times greater activity. Pre-calcination treatment of the supported catalyst resulted in minor drop in activity, yet greatly reduced bleeding (<6%) of the Pd nanoparticles from the support during multiple cycles of applications. The presence of DOM (dissolved organic matter) at up to 10 mg/L as TOC had negligible effect on the catalytic activity. The alumina supported CMC-stabilized Pd nanoparticles may serve as a class of more effective catalysts for water treatment uses.