Immobilization of hexavalent chromium in cement mortar: leaching properties and microstructures.

Stabilization and solidification (s/s) of heavy metals by cementitious materials are one of the effective methods in hazardous waste management. In cement alkaline environment, Cr(VI) compounds appear in the form of chromate anion (CrO4-2), which is highly soluble; it makes the implication of the s/s method challenging. Therefore, it is important to study the amount of chromium leaching from cementitious materials. The effects of Cr(VI) concentration and water-to-cement (w/c) ratio on the level of leaching of chromium from cement mortar (CM) were investigated in this study. Results indicated w/c not significantly affect the leaching of chromium in the age of 28-day but in the 90-day-old samples indicated a reduction in leaching of chromium from mortar with increasing w/c. Results from toxicity characteristic leaching procedure (TCLP) tests indicated that the efficiency of Cr(VI) stabilization was reduced with greater chromium content but was enhanced with increased w/c. In detail, results showed that only about 0.21% and 0.26% cement weight in TCLP and tank test of Cr(VI) was stabilized in CM, respectively. The results of X-ray diffraction (XRD) and scanning electron microscope (SEM/EDS) tests indicated that increasing the Cr(VI) content leads to changes in the formation of the cement main phases and microstructure of CM.