Study on Low Temperature Cracking Resistance of Carbon Fiber Geogrid Reinforced Asphalt Pavement Surface Combined Body.

Currently, there are limitations in the research on the use of carbon fiber geogrids to prevent low-temperature cracking in asphalt pavements. This study aims to comparatively investigate the effects of carbon fiber-based geogrid type and dense-graded asphalt concrete mixture (AC) surface combined body (SCB) type on the low-temperature cracking resistance of reinforced asphalt pavement through low-temperature bending damage tests. Two geogrid types were prepared: a carbon fiber geogrid (CCF) and a glass/carbon fiber composite qualified geogrid (GCF). Two SCB types were studied: AC-13/AC-20 and AC-20/AC-25. The results show that the improvement in the flexural tensile strength of CCF is similar to that for GCF. Moreover, under reinforced conditions, the improvement in the low-temperature cracking resistance of AC-20/AC-25 is better than that for AC-13/AC-20 by 16.26-24.57%. Based on the analysis, the reasonable ratio range of the aperture sizes to the major particle sizes in the dense gradation can achieve a more effective interlocking effect. This can improve the low-temperature cracking resistance of carbon fiber-based geogrid-reinforced samples. Then, increasing the bending absorption energy is a key way of improving the low-temperature cracking resistance of carbon fiber-based geogrid reinforcements. Eventually, the fracture type of carbon fiber-based geogrid-reinforced samples is a mixed plastic-brittle fracture. These results can provide a reference for the road failure analysis of geogrid-reinforced asphalt pavement.