Dental materials : official publication of the Academy of Dental Materials · 2013
Chemical-physical properties of experimental root canal sealers based on butyl ethylene glycol disalicylate and MTA.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Vitti Rafael P, Prati Carlo, Sinhoreti Mário Alexandre C, Zanchi Cesar H, Souza E Silva Manuela G, Ogliari Fabrício A, Piva Evandro, Gandolfi Maria G
Аннотация
OBJECTIVE: The aim of this study was to evaluate the calcium release, pH, flow, solubility, water absorption, setting and working time of three experimental root canal sealers based on mineral trioxide aggregate (MTA) and two forms of calcium phosphates (CaP).
METHODS: The materials were composed of a base and a catalyst pastes mixed in a 1:1. The base paste was made by 60% bismuth oxide and 40% butyl ethylene glycol disalicylate. Three different catalyst pastes were formulated containing 60% MTA or 40% MTA+20% CaP (hydroxyapatite HA or dibasic calcium phosphate dehydrate DCPD), 39% Resimpol 8% and 1% titanium dioxide. MTA Fillapex was used as control. The release of calcium and hydroxyl ions, solubility and water absorption were measured on regular intervals for 28 days. The working time and flow were tested according to ISO 6876:2001 and the setting time according to ASTM C266. The data were analyzed using 1-way ANOVA with Tukey's test (p<.01).
RESULTS: All the cements showed basifying activity and released calcium ions. MTA Fillapex showed the highest values of flow (p<.01) and working/setting times (p<.01) and the smallest values of solubility (p<.01) and water absorption (p<.01).
SIGNIFICANCE: All experimental materials showed satisfactory physical-chemical properties to be used as endodontic sealers in clinical practice.
METHODS: The materials were composed of a base and a catalyst pastes mixed in a 1:1. The base paste was made by 60% bismuth oxide and 40% butyl ethylene glycol disalicylate. Three different catalyst pastes were formulated containing 60% MTA or 40% MTA+20% CaP (hydroxyapatite HA or dibasic calcium phosphate dehydrate DCPD), 39% Resimpol 8% and 1% titanium dioxide. MTA Fillapex was used as control. The release of calcium and hydroxyl ions, solubility and water absorption were measured on regular intervals for 28 days. The working time and flow were tested according to ISO 6876:2001 and the setting time according to ASTM C266. The data were analyzed using 1-way ANOVA with Tukey's test (p<.01).
RESULTS: All the cements showed basifying activity and released calcium ions. MTA Fillapex showed the highest values of flow (p<.01) and working/setting times (p<.01) and the smallest values of solubility (p<.01) and water absorption (p<.01).
SIGNIFICANCE: All experimental materials showed satisfactory physical-chemical properties to be used as endodontic sealers in clinical practice.