Membrane-based microfluidic solvent extraction of Ga-68 from aqueous Zn solutions: towards an automated cyclotron production loop.

BACKGROUND

The radionuclide Ga-68 is commonly used in nuclear medicine, specifically in positron emission tomography (PET). Recently, the interest in producing Ga-68 by cyclotron irradiation of [68Zn]Zn nitrate liquid targets is increasing. However, current purification methods of Ga-68 from the target solution consist of multi-step procedures, thus, leading to a significant loss of activity through natural decay. Additionally, several processing steps are needed to recycle the costly, enriched target material.

RESULTS

To eventually allow switching from batch to continuous production, conventional batch extraction and membrane-based microfluidic extraction were compared. In both approaches, Ga-68 was extracted using N-benzoyl-N-phenylhydroxylamine in chloroform as the organic extracting phase. Extraction efficiencies of up to 99.5% ± 0.6% were achieved within 10 min, using the batch approach. Back-extraction of Ga-68 into 2 M HCl was accomplished within 1 min with efficiencies of up to 94.5% ± 0.6%. Membrane-based microfluidic extraction achieved 99.2% ± 0.3% extraction efficiency and 95.8% ± 0.8% back-extraction efficiency into 6 M HCl. When executed on a solution irradiated with a 13 MeV cyclotron at TRIUMF, Canada, comparable efficiencies of 97.0% ± 0.4% were achieved. Zn contamination in the back-extracted Ga-68 solution was found to be below 3 ppm.

CONCLUSIONS

Microfluidic solvent extraction is a promising method in the production of Ga-68 achieving high efficiencies in a short amount of time, potentially allowing for direct target recycling.