Photomedicine and laser surgery · 2017
Effect of Laser-Activated Irrigation on the Push-Out Bond Strength of ProRoot Mineral Trioxide Aggregate and Biodentine in Furcal Perforations.
Сравнительное исследованиеСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Nagas Emre, Kucukkaya Selen, Eymirli Ayhan, Uyanik Mehmet Ozgur, Cehreli Zafer Cavit
Аннотация
OBJECTIVE: The objective of the present study was to assess the effect of erbium, chromium: yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser-activated irrigation (LAI) of NaOCl on the push-out bond strength of furcal perforations repaired with ProRoot mineral trioxide aggregate (MTA) and Biodentine.
BACKGROUND DATA: Several studies investigated the adhesion of calcium silicate-based cements after exposure to endodontic irrigants, while effect of LAI on bond strength remains to be elucidated.
MATERIALS AND METHODS: Bur-cut furcal perforations with standard dimensions were created in 100 extracted human mandibular molars. Teeth were randomly distributed into two groups (n = 50/group) according to the repair material applied: (1) ProRoot MTA or (2) Biodentine. The specimens were further assigned into five subgroups according to the irrigation regimens used over the set materials: (a) distilled water with needle irrigation; (b) 5.25% NaOCl with needle irrigation; (c) distilled water with LAI; (d) 5.25% NaOCl with LAI; and (e) no irrigation (control). Bond strengths of the test materials were assessed by using push-out bond strength test.
RESULTS: Biodentine showed significantly higher dislocation resistance than ProRoot MTA (p < 0.05). Laser activation of 5.25% NaOCl and distilled water did not significantly affect the push-out bond strength results (p > 0.05).
CONCLUSIONS: Biodentine showed higher dislocation resistance than ProRoot MTA as a perforation repair material. Er,Cr:YSGG laser activation of irrigation aqueous solutions had no adverse effect on push-out bond strength of Biodentine and ProRoot MTA.
BACKGROUND DATA: Several studies investigated the adhesion of calcium silicate-based cements after exposure to endodontic irrigants, while effect of LAI on bond strength remains to be elucidated.
MATERIALS AND METHODS: Bur-cut furcal perforations with standard dimensions were created in 100 extracted human mandibular molars. Teeth were randomly distributed into two groups (n = 50/group) according to the repair material applied: (1) ProRoot MTA or (2) Biodentine. The specimens were further assigned into five subgroups according to the irrigation regimens used over the set materials: (a) distilled water with needle irrigation; (b) 5.25% NaOCl with needle irrigation; (c) distilled water with LAI; (d) 5.25% NaOCl with LAI; and (e) no irrigation (control). Bond strengths of the test materials were assessed by using push-out bond strength test.
RESULTS: Biodentine showed significantly higher dislocation resistance than ProRoot MTA (p < 0.05). Laser activation of 5.25% NaOCl and distilled water did not significantly affect the push-out bond strength results (p > 0.05).
CONCLUSIONS: Biodentine showed higher dislocation resistance than ProRoot MTA as a perforation repair material. Er,Cr:YSGG laser activation of irrigation aqueous solutions had no adverse effect on push-out bond strength of Biodentine and ProRoot MTA.