Bolla Pradeep Kumar, Gote Vrinda, Singh Mahima, Yellepeddi Venkata Kashyap, Patel Manan, Pal Dhananjay, Gong Xiaoming, Sambalingam Devaraj, Renukuntla Jwala
Аннотация
AIM: To prepare and characterise lutein-loaded polylactide-co-glycolide-polyethylene glycol-folate (PLGA-PEG-FOLATE) nanoparticles and evaluate enhanced uptake in SK-N-BE(2) cells.
METHODS: Nanoparticles were prepared using O/W emulsion solvent evaporation and characterised using DLS, SEM, DSC, FTIR and in-vitro release. Lutein-uptake in SK-N-BE(2) cells was determined using flow-cytometry, confocal-microscopy and HPLC. Control was lutein PLGA nanoparticles.
RESULTS: The size of lutein-loaded PLGA and PLGA-PEG-FOLATE nanoparticles were 189.6 ± 18.79 nm and 188.0 ± 4.06 nm, respectively. Lutein entrapment was ∼61%(w/w) and ∼73%(w/w) for PLGA and PLGA-PEG-FOLATE nanoparticles, respectively. DSC and FTIR confirmed encapsulation of lutein into nanoparticles. Cellular uptake studies showed ∼1.6 and ∼2-fold enhanced uptake of lutein from PLGA-PEG-FOLATE nanoparticles compared to PLGA nanoparticles and lutein, respectively. Cumulative release of lutein was higher in PLGA nanoparticles (100% (w/w) within 24 h) compared to PLGA-PEG-FOLATE nanoparticles (∼80% (w/w) in 48 h).
CONCLUSION: Lutein-loaded PLGA-PEG-FOLATE nanoparticles could be a potential treatment for hypoxic ischaemic encephalopathy.
METHODS: Nanoparticles were prepared using O/W emulsion solvent evaporation and characterised using DLS, SEM, DSC, FTIR and in-vitro release. Lutein-uptake in SK-N-BE(2) cells was determined using flow-cytometry, confocal-microscopy and HPLC. Control was lutein PLGA nanoparticles.
RESULTS: The size of lutein-loaded PLGA and PLGA-PEG-FOLATE nanoparticles were 189.6 ± 18.79 nm and 188.0 ± 4.06 nm, respectively. Lutein entrapment was ∼61%(w/w) and ∼73%(w/w) for PLGA and PLGA-PEG-FOLATE nanoparticles, respectively. DSC and FTIR confirmed encapsulation of lutein into nanoparticles. Cellular uptake studies showed ∼1.6 and ∼2-fold enhanced uptake of lutein from PLGA-PEG-FOLATE nanoparticles compared to PLGA nanoparticles and lutein, respectively. Cumulative release of lutein was higher in PLGA nanoparticles (100% (w/w) within 24 h) compared to PLGA-PEG-FOLATE nanoparticles (∼80% (w/w) in 48 h).
CONCLUSION: Lutein-loaded PLGA-PEG-FOLATE nanoparticles could be a potential treatment for hypoxic ischaemic encephalopathy.