In Vitro Bacterial Adhesion and Biofilm Formation on Fully Absorbable Poly-4-hydroxybutyrate and Nonabsorbable Polypropylene Pelvic Floor Implants.

Knitted polypropylene (PP) implants for the correction of pelvic organ prolapse have been associated with complications such as vaginal exposure, infection, and pain. Since certain complications may be linked to bacterial contamination and persistent inflammation, there is a rationale to develop a biocompatible implant that is less prone to bacterial adhesion and biofilm formation. Delayed absorbable materials could meet these requirements and poly-4-hydroxybutyrate (P4HB) might be such a new material for future pelvic floor implants. We studied in vitro bacterial adhesion and biofilm formation on P4HB in comparison to PP. We investigated the influence of both polymers using flat films and compared P4HB and PP implants with different knitting designs. P4HB flat films were demonstrated to be hydrophilic with significantly less Staphylococcus aureus and Escherichia coli cultured from P4HB films than from hydrophobic PP films after 24 h of incubation. On the implants, a higher number of E. coli were cultured after 1 h of incubation from the knitted P4HB implant with the highest density and smallest pore size, compared to other P4HB and PP implants. No differences were observed between the implants for E. coli at later time points or for S. aureus incubation. These results show that in flat films, the polymer influences biofilm formation, demonstrated by a reduced biofilm formation on P4HB compared with PP flat films. In addition, the knitting design may affect bacterial adhesion. Despite certain design and material characteristics that give the knitted P4HB implants a higher surface area, this did not result in more bacterial adhesion and biofilm formation overall. Collectively, these results warrant further (pre)clinical investigations of P4HB pelvic floor implants.