A new material to prevent urethral damage after implantation of artificial devices: an experimental study.

OBJECTIVE

To validate the application of the bacterial cellulose (BC) membrane as a protecting bar-rier to the urethra.

MATERIALS AND

METHODS

Forty female Wistar rats (four groups of 10): Group 1 (sham), the urethra was dissected as in previous groups and nothing applied around; Group 2, received a 0.7cm strip of the BC applied around the urethra just below the bladder neck; Group 3, received a silicon strip with the same dimensions as in group 2; Group 4, had a combination of 2 and 3 groups being the silicon strip applied over the cellulosic material. Half of the animals in each group were killed at 4 and 8 months. Bladder and urethra were fixed in formalin for histological analysis.

RESULTS

Inflammatory infiltrates were more intense at 4 months at lymphonodes (80% Grade 2), statistically different in the group 2 compared with groups 1 (p=0.0044) and 3 (p=0.0154). At 8 months, all samples were classified as grade 1 indicating a less intense inflammatory reaction in all groups. In group 2, at 8 months, there was a reduction in epithelial thickness (30±1μm) when com-pared to groups 1 (p=0.0001) and 3 (p<0.0001). Angiogenesis was present in groups 2 and 4 and absent in group 3. In BC implant, at 4 and 8 months, it was significant when comparing groups 4 with 1 (p=0.0159).

CONCLUSION

BC membrane was well integrated to the urethral wall promoting tissue remodeling and strengthening based on morphometric and histological results and may be a future option to prevent urethral damage.