Synthesis, characterization and spectroscopic investigation of Cr3+ doped wollastonite nanophosphor.

This work explores the preparation of nanocrystalline Cr(3+) (1-5 mol%) doped CaSiO3 phosphors by solution combustion process and study of its photoluminescence (PL) behavior. The nanopowders are well characterized by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infra-red (FTIR) spectroscopy. PXRD results confirm monoclinic phase upon calcination at 950°C for 3h. SEM micrographs indicates that the powder is highly porous and agglomerated. The TEM images show the powder to consist of spherical shaped particles of size ∼30-60 nm. Upon 323 nm excitation, the emission profile of CaSiO3:Cr(3+) exhibits a narrow red emission peak at 641nm due to (2)E→(4)A2 transition and broad band at 722 nm due to (4)T2g→(4)A2g. It is observed that PL intensity increases with increase in Cr(3+) concentration and highest PL intensity is observed for 3 mol% doped sample. The PL intensity decreases with further increase in Cr(3+) doping. This decrease in PL intensity beyond 3 mol% is ascribed to concentration quenching. Racah parameters are calculated to describe the effects of electron-electron repulsion within the crystal lattice. The parameters show 21% reduction in the Racah parameter of free ion and the complex, indicating the moderate nephelauxetic effect in the lattice.