Journal of endodontics · 2013
Solubility and disintegration of new calcium aluminate cement (EndoBinder) containing different radiopacifying agents.
Сравнительное исследованиеСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Garcia Lucas da Fonseca Roberti, Chinelatti Michelle Alexandra, Rossetto Hebert Luis, Pires-de-Souza Fernanda de Carvalho Panzeri
Аннотация
INTRODUCTION: The aim of this study was to evaluate the solubility and disintegration of EndoBinder (EB) containing 3 different radiopacifying agents, bismuth oxide (Bi2O3), zinc oxide (ZnO), or zirconium oxide (ZrO2), in comparison with gray mineral trioxide aggregate (GMTA) and white MTA (WMTA).
METHODS: Ten specimens of each cement were made in a stainless steel matrix (20 × 1.5 mm) according to Specification no. 57 of American National Standards Institute/American Dental Association: EB + Bi2O3, EB + ZrO, EB + ZnO, WMTA, and GMTA. The specimens were weighed on an accurate analytical scale and immersed in 50 mL distilled and deionized water at 37°C for 7 days. Afterwards, specimens were dried and weighed again to determine mass loss (%). Resulting solutions were analyzed in an atomic absorption spectrophotometer for identification and quantification of chemical elements released.
RESULTS: All cements presented mean values of solubility and disintegration above the American National Standards Institute/American Dental Association Specification no. 57. EB + Bi2O3 presented the lowest mass loss (5.08%) and WMTA (6.65%) the highest, with no statistically significant difference (P > .05). The release of several chemical elements was observed, mostly metal ions. Only GMTA and EB + Bi2O3 showed the presence of Cr, with significant difference (P < .05). EB + ZnO presented the highest levels of Pb, followed by WMTA (P < .05). For As, the cements presented different release levels, with EB + ZnO showing the highest and GMTA the lowest levels (P < .05). However, the amounts of As and Pb released were lower than the safe limit proposed by ISO 9917-1.
CONCLUSIONS: Irrespective of the radiopacifying agents used, EndoBinder presented similar behavior to MTA.
METHODS: Ten specimens of each cement were made in a stainless steel matrix (20 × 1.5 mm) according to Specification no. 57 of American National Standards Institute/American Dental Association: EB + Bi2O3, EB + ZrO, EB + ZnO, WMTA, and GMTA. The specimens were weighed on an accurate analytical scale and immersed in 50 mL distilled and deionized water at 37°C for 7 days. Afterwards, specimens were dried and weighed again to determine mass loss (%). Resulting solutions were analyzed in an atomic absorption spectrophotometer for identification and quantification of chemical elements released.
RESULTS: All cements presented mean values of solubility and disintegration above the American National Standards Institute/American Dental Association Specification no. 57. EB + Bi2O3 presented the lowest mass loss (5.08%) and WMTA (6.65%) the highest, with no statistically significant difference (P > .05). The release of several chemical elements was observed, mostly metal ions. Only GMTA and EB + Bi2O3 showed the presence of Cr, with significant difference (P < .05). EB + ZnO presented the highest levels of Pb, followed by WMTA (P < .05). For As, the cements presented different release levels, with EB + ZnO showing the highest and GMTA the lowest levels (P < .05). However, the amounts of As and Pb released were lower than the safe limit proposed by ISO 9917-1.
CONCLUSIONS: Irrespective of the radiopacifying agents used, EndoBinder presented similar behavior to MTA.