Effect of bio-based derived epoxy resin on interfacial adhesion of cellulose film and applicability towards natural jute fiber-reinforced composites.

This paper reports a bio-based vanillin-derived epoxy (VDE) resin for bio-based natural fiber-reinforced composites. VDE monomer was synthesized, and curing agents, namely, 4,4´-diaminodiphenyl methane (DDM) and isophorone diamine, were used. The prepared VDE resins with various curing parameters were characterized using FTIR, NMR, tensile test, bending test and water contact angle. Further, the interfacial adhesion feasibility of VDE resins on cellulose film was studied through the single-lap shear joint examination and compared with a commercial epoxy, DGEBA. The VDE-DDM resin exhibited excellent interfacial adhesion with cellulose than VDE-IPDA and DGEBA-DDM resins. The cured VDE-DDM thermoset showed a tensile strength of 86.0 ± 6.5 MPa, thermal stability of 241.0 °C at Td5%, and an elastic modulus of 2.9 ± 0.3 GPa, which is better than the commercial epoxy resin. Besides, the developed VDE-DDM resin was used to fabricate treated-jute fiber (TJF)-reinforced composites. The bio-based VDE-DDM/TJF composite's flexural strength was higher than the commercial epoxy resin composite, DGEBA-DDM/TJF. Furthermore, the phosphorus moiety of the VDE-DDM resin endows flame retardancy to the VDE-DDM/TJF composite during combustion. Overall, the appealing properties of bio-based VDE-DDM/TJF composite render environment-friendly and high-performance structural applications.