[Dynamic leaching behavior of heavy metals in eco-cement mortar block].

A dynamic leaching test with the renewal of acidic leaching medium was designed to study the leaching behavior of the seven heavy metals (As, Cd, Cr, Cu, Ni, Pb, Zn) in three solidified eco-cement mortar samples with different particle size (fine granule, coarse granule, block) under a long-term leaching condition. It was demonstrated that all the heavy metals were detected in the leachate except Cd. The leaching ratio of Cr was the highest when compared with other metals in the same sample, and the leaching ratio of every metal showed an identical tendency: fine granule> coarse granule > block. The on-going leaching part of the relationship curve of accumulative leaching point (Pt) and t1/2 of each metal presented a fairly good linearity, which indicated that the leaching process was under the control of diffusion mechanism by the Fick Law. To each metal, the effective diffusion coefficient (Deff) showed a tendency of fine granule < coarse granule < block, which was opposite to the tendency of leaching ratio. It could be concluded that the solidified eco-cement mortar with a bigger size would have a lower leaching ratio and a shorter period to finish the leaching test. To all the metals, the Deff was very low, with the magnitude around 10(-10) cm2/s, which meant the leaching process would take a relatively long time.