Daily exposure to fluoride mouthrinse produces sustained fluoride release from orthodontic adhesives in vitro.
Сравнительное исследованиеСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Benington P C, Gillgrass T J, Foye R H, Millett D T, Gilmour W H
Аннотация
OBJECTIVES: To determine firstly, if sustained fluoride release can be achieved from five orthodontic adhesives: Ketac-Cem, Fuji ORTHO LC, Sequence, Transbond and Right-On, with daily exposure to fluoride mouthrinse in vitro, and secondly, if sustained fluoride release can be re-established from the same specimens, after an interruption in mouthrinse exposure.
METHODS: Ten brackets were bonded to bovine incisors using each adhesive. Each adhesive group was divided equally into a test and a control sub-group. In phase 1 (42 days), the test sub-groups were exposed for 1min daily to fluoride mouthrinse (225 ppm), followed by immersion in de-ionised water for 42 days to deplete their fluoride reserves. Mouthrinse exposure was then resumed in phase 2 (28 days). Mean cumulative fluoride release (MCFR) was calculated for days 0-21 of phase 1 and for the plateau portion of the fluoride release curves in phase 1 (days 21-42) and phase 2 (days 7-28).
RESULTS: During phase 1, the MCFR for each test sub-group was significantly greater than its control (p<0.05). There was no significant difference in MCFR between the curve plateau portion of phases 1 and 2 for all adhesives except Transbond, for which MCFR was less in phase 2 (p<0. 05).
CONCLUSIONS: Sustained fluoride release occurred for each adhesive exposed daily to fluoride mouthrinse, at a level significantly greater than its control. After fluoride exhaustion, re-exposure to daily fluoride mouthrinse produced sustained fluoride release levels comparable to those prior to exhaustion, for all adhesives except Transbond.
METHODS: Ten brackets were bonded to bovine incisors using each adhesive. Each adhesive group was divided equally into a test and a control sub-group. In phase 1 (42 days), the test sub-groups were exposed for 1min daily to fluoride mouthrinse (225 ppm), followed by immersion in de-ionised water for 42 days to deplete their fluoride reserves. Mouthrinse exposure was then resumed in phase 2 (28 days). Mean cumulative fluoride release (MCFR) was calculated for days 0-21 of phase 1 and for the plateau portion of the fluoride release curves in phase 1 (days 21-42) and phase 2 (days 7-28).
RESULTS: During phase 1, the MCFR for each test sub-group was significantly greater than its control (p<0.05). There was no significant difference in MCFR between the curve plateau portion of phases 1 and 2 for all adhesives except Transbond, for which MCFR was less in phase 2 (p<0. 05).
CONCLUSIONS: Sustained fluoride release occurred for each adhesive exposed daily to fluoride mouthrinse, at a level significantly greater than its control. After fluoride exhaustion, re-exposure to daily fluoride mouthrinse produced sustained fluoride release levels comparable to those prior to exhaustion, for all adhesives except Transbond.
Предметные рубрики MeSH
Acrylic ResinsAluminum SilicatesAnalysis of VarianceAnimalsArea Under CurveBisphenol A-Glycidyl MethacrylateCattleDental BondingDentin-Bonding AgentsFluoridesGlass Ionomer CementsIon-Selective ElectrodesMagnesium OxideMethacrylatesMouthwashesOrthodontic BracketsPolycarboxylate CementPolyurethanesResin CementsZinc Oxide