Reinforcement of Cement Nanocomposites through Optimization of Mixing Ratio between Carbon Nanotube and Polymer Dispersing Agent.

Carbon nanotubes (CNTs), known for their exceptional mechanical, thermal, and electrical properties, are being explored as cement nanofillers in the construction field. However, due to the limited water dispersion of CNTs, polymer dispersing agents like polycarboxylate ether (PCE) and sulfonated naphthalene formaldehyde (SNF) are essential for uniform dispersion. In a previous study, PCE and SNF, common cement superplasticizers, effectively dispersed CNTs in cement nanocomposites. However, uncertainties remained regarding the extent to which all dispersing agents interacted efficiently with CNTs. Therefore, this research quantitatively assessed CNT interaction with dispersing agents through dispersion and centrifugation. Approximately 37% of PCE and 50% of SNF persisted compared to CNT after centrifugation. The resulting cement nanocomposites, with optimized mixing ratios, exhibited enhanced compressive strength of about 14% for CNT/PCE (78.13 MPa) and 12.3% for CNT/SNF (76.97 MPa) compared to plain cement (68.52 MPa). XRD results linked strength reinforcement to increased cement hydrate from optimized CNT dispersion. FE-SEM analysis revealed that CNTs were positioned within the pores of the cement. These optimized cement nanocomposites hold promise for improved safety in the construction industry.