Comparison of the properties of phenolic resin synthesized from different aldehydes and evaluation of the release and health risks of VOCs.

Different amounts of glyoxal and paraformaldehyde were used to synthesize phenol-glyoxal (PG) and phenol-paraformaldehyde (PPF) resins, which were compared with conventional phenol-formaldehyde (PF) resins. Glyoxal oxidation leads to a pH value of 9.83 for PG 2.2. With the addition of polyformaldehyde, PPF 2.2 exhibited the highest viscosity at 17333.33 mPa s. The PPF 2.0 plywood has a maximum bonding strength of 1.94 MPa. The formaldehyde emission of PG 1.8 plywood is found to have a minimum value of 0.025 mg/m3, reaching the ENF limit (≤0.025 mg/m3). Acetaldehyde is found only in volatile organic compound (VOC) emissions from PG plywood and is associated with increased glyoxal. PPF plywood emitted more aromatic and total VOC (TVOC) than the other two plywood types. The measured TVOC for PPF 2.2 is 196.07 μg/m3. The results showed that the total cancer risk (TCR) values of PPF 1.8, PPF 2.0, and PG 1.8 were above the threshold of 1.00E-4, indicating a definite carcinogenic risk. Acetaldehyde in the PG plywood exceeded the safety threshold for noncarcinogenic risk. The use of paraformaldehyde in the wood-based panel production is been considered a possible means of improving the bonding strength of plywood. Glyoxal has also been shown to be a viable method for lowering the formaldehyde emissions from plywood. The VOC emissions from plywood changed significantly depending on the aldehyde used. Limiting VOCs that present high health hazards is crucial for reducing the negative impact of plywood on both indoor environments and human health.