Tailored Coatings for Enhanced Performance of Zinc-Magnesium Alloys in Absorbable Implants.

Absorbable metals exhibit potential for next-generation temporary medical implants, dissolving safely in the body during tissue healing and regeneration. Their commercial incorporation could substantially diminish the need for additional surgeries and complications that are tied to permanent devices. Despite extensive research on magnesium (Mg) and iron (Fe), achieving the optimal combination of mechanical properties, biocompatibility, and controlled degradation rate for absorbable implants remains a challenge. Zinc (Zn) and Zn-based alloys emerged as an attractive alternative for absorbable implants, due to favorable combination of in vivo biocompatibility and degradation behavior. Moreover, the development of suitable coatings can enhance their biological characteristics and tailor their degradation process. In this work, four different biodegradable coatings (based on zinc phosphate (ZnP), collagen (Col), and Ag-doped bioactive glass nanoparticles (AgBGNs)) were synthesized by chemical conversion, spin-coating, or a combination of both on Zn-3Mg substrates. This study assessed the impact of the coatings on in vitro degradation behavior, cytocompatibility, and antibacterial activity. The ZnP-coated samples demonstrated controlled weight loss and a decreased corrosion rate over time, maintaining a physiological pH. Extracts from the uncoated, ZnP-coated, and Col-AgBGN-coated samples showed higher cell viability with increasing concentration. Bacterial viability was significantly impaired in all coated samples, particularly in the Col-AgBGN coating. This study showcases the potential of a strategic material-coating combination to effectively tackle multiple challenges encountered in current medical implant technologies by modifying the properties of absorbable metals to tailor patient treatments.