Copper-doped magnesium phosphate nanopowders for critical size calvarial bone defect intervention.

Calvarial defects of bone present difficult clinical situations, and their restoration using biocompatible materials requires special treatments that enable bone regeneration. Magnesium phosphate (MgP) is known as an osteoinductive biomaterial because it contains Mg2+ ions and P ions that enhance the activity of osteoplast cells and help in bone regeneration. In this study, MgP and CuO-doped MgP were fabricated and characterized for their physicomechanical properties, particle size, morphology, surface area, antibacterial test, and in vitro bioactivity evaluation using the following techniques: X-rays diffraction, Fourier-transformer infrared, TEM, and Brunauer, Emmett and Teller (BET) surface area, X-rays photoelectron spectroscopy (XPS), and Scanning electron microscopy (SEM). Furthermore, these nanopowders were implanted in adult inbred male Wistar rats and studied after two periods (28 and 56 days). The results demonstrated that the obtained semiamorphous powders are in nanoscale (≤ 50 nm). XPS analysis ensured the preparation of MgP as mono MgP and CuO were incorporated in the structure as Cu2+ . The bioactivity was supported by the observation of calcium phosphate layer on the nanopowders' surface. The in vivo study demonstrated success of MgP nanopowders especially those doped with CuO in restoration of calvarial defect bone. Therefore, fabricated biomaterials are of great potential in restoration of bone calvarial defects.