Photoreduction of 99Tc pertechnetate by nanometer-sized metal oxides: new strategies for formation and sequestration of low-valent technetium.

Technetium-99 ((99)Tc) (β(-)(max): 293.7 keV; t(1/2): 2.1 × 10(5) years) is a byproduct of uranium-235 fission and comprises a large component of radioactive waste. Under aerobic conditions and in a neutral-basic environment, the pertechnetate anion ((99)TcO(4)(-)) is stable. (99)TcO(4)(-) is very soluble, migrates easily through the environment and does not sorb well onto mineral surfaces, soils, or sediments. This study moves forward a new strategy for the reduction of (99)TcO(4)(-) and the chemical incorporation of the reduced (99)Tc into a metal oxide material. This strategy employs a single material, a polyoxometalate (POM), α(2)-[P(2)W(17)O(61)](10-), that can be photoactivated in the presence of 2-propanol to transfer electrons to (99)TcO(4)(-) and incorporate the reduced (99)Tc covalently into the α(2)-framework to form the (99)Tc(V)O species, (99)Tc(V)O(α(2)-P(2)W(17)O(61))(7-). This occurs via the formation of an intermediate species that slowly converts to (99)Tc(V)O(α(2)-P(2)W(17)O(61))(7-). Extended X-ray absorption fine structure and X-ray absorption near-edge spectroscopy analysis suggests that the intermediate consists of a (99)Tc(IV) α(2)- species where the (99)Tc is likely bound to two of the four W-O oxygen atoms in the α(2)-[P(2)W(17)O(61)](10-) defect. This intermediate then oxidizes and converts to the (99)Tc(V)O(α(2)-P(2)W(17)O(61))(7-) product. The reduction and incorporation of (99)TcO(4)(-) was accomplished in a "one pot" reaction using both sunlight and UV irradiation and monitored as a function of time using multinuclear nuclear magnetic resonance and radio thin-layer chromatography. The process was further probed by the "step-wise" generation of reduced α(2)-P(2)W(17)O(61)(12-) through bulk electrolysis followed by the addition of (99)TcO(4)(-). The reduction and incorporation of ReO(4)(-), as a nonradioactive surrogate for (99)Tc, does not proceed through the intermediate species, and Re(V)O is incorporated quickly into the α(2)-[P(2)W(17)O(61)](10-) defect. These observations are consistent with the periodic trends of (99)Tc and Re. Specifically, (99)Tc is more easily reduced compared to Re. In addition to serving as models for metal oxides, POMs may also provide a suitable platform to study the molecular level dynamics and the mechanisms of the reduction and incorporation of (99)Tc into a material.