Increasing the open-circuit voltage in high-performance organic photovoltaic devices through conformational twisting of an indacenodithiophene-based conjugated polymer.

A fused ladder indacenodithiophene (IDT)-based donor-acceptor (D-A)-type alternating conjugated polymer, PIDTHT-BT, presenting n-hexylthiophene conjugated side chains is prepared. By extending the degree of intramolecular repulsion through the conjugated side chain moieties, an energy level for the highest occupied molecular orbital (HOMO) of -5.46 eV--a value approximately 0.27 eV lower than that of its counterpart PIDTDT-BT--is obtained, subsequently providing a fabricated solar cell with a high open-circuit voltage of approximately 0.947 V. The hole mobility (determined using the space charge-limited current model) in a blend film containing 20 wt% PIDTHT-BT) and 80 wt% [6,6]-phenyl-C71 butyric acid methyl ester (PC71 BM) is 2.2 × 10(-9) m(2) V(-1) s(-1), which is within the range of reasonable values for applications in organic photovoltaics. The power conversion efficiency is 4.5% under simulated solar illumination (AM 1.5G, 100 mW cm(-2)).