Dental materials : official publication of the Academy of Dental Materials · 2024
A bioactive and anti-bacterial nano-sized zirconium phosphate/GO (nZrP/GO) composite: Potential use as a coating for dental implants?
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Al-Noaman Ahmed, Rawlinson Simon Charles Fielding
Аннотация
OBJECTIVE: Dental implants fabricated from titanium have several limitations and therefore, alternative materials that fulfil the criteria of successful dental implant (bioactivity and anti-bacterial activity) need to be considered. Polyether ether ketone (PEEK) has been suggested to replace titanium implants. However, this material needs surface modification to meet the appropriate criteria. A nano-sized zirconium phosphate/GO (nZrP/GO) composite coating was prepared to improve PEEK's biological qualities.
METHODS: Polished and cleaned PEEK discs were coated with the composite of nZrP doped with 1.25 wt% GO by the soft-template method. To analyze the composite coating, X-ray, atomic force microscopy, and field emission scanning electron microscopy-energy dispersive spectroscopy were used. The adhesion of the coating to PEEK was measured by adhesive tape test. By measuring the optical contact angle, the coated and non-coated samples' differences in wettability were evaluated. Antimicrobial activity was evaluated against S. aureus and E. coli and cytotoxicity tested employing gingival fibroblasts and osteoblast-like cells.
RESULTS: The nZrP/GO composite coating was 23.45 µm thick, was irregular and attached strongly to the PEEK surface. Following coating, the water contact angle dropped to 34° and surface roughness to 13 nm. The coating reduced the count of bacteria two-fold and was non-cytotoxic to mammalian osteoblast-like cells and fibroblasts. A precipitation of nano-calcium-deficient apatite was observed on the surface of the nZrP/GO coating following a 28-day immersion in SBF.
SIGNIFICANCE: PEEK-coated with nZr/GO coating is a good candidate as dental implant.
METHODS: Polished and cleaned PEEK discs were coated with the composite of nZrP doped with 1.25 wt% GO by the soft-template method. To analyze the composite coating, X-ray, atomic force microscopy, and field emission scanning electron microscopy-energy dispersive spectroscopy were used. The adhesion of the coating to PEEK was measured by adhesive tape test. By measuring the optical contact angle, the coated and non-coated samples' differences in wettability were evaluated. Antimicrobial activity was evaluated against S. aureus and E. coli and cytotoxicity tested employing gingival fibroblasts and osteoblast-like cells.
RESULTS: The nZrP/GO composite coating was 23.45 µm thick, was irregular and attached strongly to the PEEK surface. Following coating, the water contact angle dropped to 34° and surface roughness to 13 nm. The coating reduced the count of bacteria two-fold and was non-cytotoxic to mammalian osteoblast-like cells and fibroblasts. A precipitation of nano-calcium-deficient apatite was observed on the surface of the nZrP/GO coating following a 28-day immersion in SBF.
SIGNIFICANCE: PEEK-coated with nZr/GO coating is a good candidate as dental implant.