Assembly of tin oxide/graphene nanosheets into 3D hierarchical frameworks for high-performance lithium storage.

3D hierarchical tin oxide/graphene frameworks (SnO2 /GFs) were built up by the in situ synthesis of 2D SnO2 /graphene nanosheets followed by hydrothermal assembly. These SnO2 /GFs exhibited a 3D hierarchical porous architecture with mesopores (≈3 nm), macropores (3-6 μm), and a large surface area (244 m(2) g(-1) ), which not only effectively prevented the agglomeration of SnO2 nanoparticles, but also facilitated fast ion and electron transport in 3D pathways. As a consequence, the SnO2 /GFs exhibited a high capacity of 830 mAh g(-1) for up to 70 charge-discharge cycles at 100 mA g(-1) . Even at a high current density of 500 mA g(-1) , a reversible capacity of 621 mAh g(-1) could be maintained for SnO2 /GFs with excellent cycling stability. Such performance is superior to that of previously reported SnO2 /graphene and other SnO2 /carbon composites with similar weight contents of SnO2 .