Thermal effect of light irradiation time on the setting time of mineral trioxide aggregate and calcium-enriched mixture cements.

This study aimed to assess the thermal effect of different light irradiation times on the setting time of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cements. This in vitro experimental study evaluated 40 hydraulic cement specimens, including 20 MTA and 20 CEM specimens, according to the manufacturers'instructions. For each cement, the specimens were divided into 3 test groups light cured with a halogen light-curing unit (n = 5 per group) and 1 control group (n = 5) that was not exposed to irradiation. The specimens in the MTA test groups were light cured for 20, 40, or 60 seconds, and the specimens in the CEM test groups were light cured for 60, 90, or 120 seconds. All test and control groups had 60 seconds of rest time. Setting of the cements was assessed at different timepoints using a Gillmore needle weighing 113.4 g with a 12.2-mm diameter according to ASTM C266-03 standards. The data were analyzed with the Fisher exact test and the Mann-Whitney U test (α = 0.05). The setting of MTA specimens after different curing times was significantly different (P < 0.05). The setting time of MTA control specimens was significantly longer than that of test specimens (P = 0.008). The setting of CEM specimens after different curing times was not significantly different (P > 0.05). However, the setting time for CEM control specimens was significantly longer than that for test specimens (P = 0.008). Light curing with a halogen light-curing unit can significantly decrease the setting time for MTA and CEM cements.