TiO2 scaffolds in peri-implant dehiscence defects: an experimental pilot study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Verket Anders, Müller Benjamin, Wohlfahrt Johan Caspar, Lyngstadaas Ståle Petter, Ellingsen Jan Eirik, Jostein Haugen Håvard, Tiainen Hanna
Аннотация
OBJECTIVES: The primary objective was to assess osseointegration of implants with dehiscence defects grafted with a TiO2 scaffold. The secondary objective was to assess the performance of the scaffold in terms of mechanical stability and bone fill.
MATERIAL AND METHODS: Five minipigs had the mandibular premolars extracted. After healing, two dental implants (SLActive® , Institut Straumann AG, Basel, Switzerland) with associated semi-cylindrical dehiscence defects (Ø = 6 mm, height = 10 mm) were installed in each quadrant. The defects were grafted with test scaffolds (n = 10) or control autologous bone blocks (n = 10). After 3 months submerged healing, the pigs were euthanized and the sites analysed by microcomputed tomography and histology.
RESULTS: Four minipigs were available for second stage surgery; (n = 9) experimental and (n = 7) control sites. The mean bone-to-implant contact on the defect side was 82% (±10%) and 79% (±11%) in the test and control groups respectively. The mean level of first bone-to-implant contact was more coronal on the defect side in the test group 3.2 mm (±0.4 mm) than in the control group 3.6 mm (±1.1 mm). The defect area occupied by bone within the extent of the scaffold varied, but averaged 37% (±14.6%) whereas the material itself occupied 7.4% (±3.5%).
CONCLUSIONS: Within the limitations of the study, the results suggest that the novel synthetic scaffold material perform similar to the autologous bone block control with respect to implant osseointegration. The mechanical properties of the scaffold appeared sufficient to withstand clinical load in the present experimental model.
MATERIAL AND METHODS: Five minipigs had the mandibular premolars extracted. After healing, two dental implants (SLActive® , Institut Straumann AG, Basel, Switzerland) with associated semi-cylindrical dehiscence defects (Ø = 6 mm, height = 10 mm) were installed in each quadrant. The defects were grafted with test scaffolds (n = 10) or control autologous bone blocks (n = 10). After 3 months submerged healing, the pigs were euthanized and the sites analysed by microcomputed tomography and histology.
RESULTS: Four minipigs were available for second stage surgery; (n = 9) experimental and (n = 7) control sites. The mean bone-to-implant contact on the defect side was 82% (±10%) and 79% (±11%) in the test and control groups respectively. The mean level of first bone-to-implant contact was more coronal on the defect side in the test group 3.2 mm (±0.4 mm) than in the control group 3.6 mm (±1.1 mm). The defect area occupied by bone within the extent of the scaffold varied, but averaged 37% (±14.6%) whereas the material itself occupied 7.4% (±3.5%).
CONCLUSIONS: Within the limitations of the study, the results suggest that the novel synthetic scaffold material perform similar to the autologous bone block control with respect to implant osseointegration. The mechanical properties of the scaffold appeared sufficient to withstand clinical load in the present experimental model.