Omental coating attenuates implant-induced foreign body reaction in rats.

The objective of this study is to clarify whether the omental coating can effectively attenuate foreign body reaction (FBR) induced by implanted materials. Male Sprague-Dawley rats were injected with polydextran particle slurry intraperitoneally to activate the omentum. 7 days later, polyether polyurethane sponge discs were implanted subcutaneously on each side of the rat's back as the foreign implants to induce FBR. The next day, omental transposition were performed. The disc on the left side of each rat's back was wrapped with omental flap (omental group); the disc on the right side was untreated (control group). All discs were removed 21 days after implantation and assessed by determining the components of the fibrovascular tissue (angiogenesis, inflammation, foreign body giant cells (FBGCs) aggregation and fibrogenesis). In implants in omental group, micro vessel density (MVD), Hemoglobin (Hb) content and VEGF levels (pro-angiogenic cytokine) were increased when compared with implants from control group. Inflammatory parameters (IL-1β; macrophage accumulation-NAG activity; neutrophil accumulation- MPO levels) were decreased in implants after omental coating. Also, collagen deposition, fibrous capsule thickness, and FBGCs decreased in implants from omental group. However, intra-implant levels of TNF-α and TGF-β1 were not different after omental coating. Our findings showed for the first time that the omental coating around the implants attenuate the adverse FBR, it may be critical in developing new strategies to control FBR and improve the function and performance of the implanted materials.