Journal of the mechanical behavior of biomedical materials · 2015
γ-Irradiation sterilized bone strengthened and toughened by ribose pre-treatment.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Willett Thomas L, Burton Brianne, Woodside Mitchell, Wang Zhirui, Gaspar Anne, Attia Tarik
Аннотация
OBJECTIVE: This study tested the hypothesis that a ribose-based pre-treatment would protect the strength, ductility and toughness of γ-irradiation sterilized cortical bone.
METHODS: Experiment 1: The effects of ribose pre-treatment (1.8M in PBS at 60°C for 24h) prior to 33 kGy of irradiation on strength, ductility and toughness (beams in three-point bending) and fracture toughness (J-integral at instability in single edge notched (bending)) were tested against matched non-irradiated and irradiated controls from bovine tibiae. Experiment 2: Three-point bending tests were conducted using beams from human femora (males, 59-67 years). Bone collagen thermal stability and network connectivity were examined using hydrothermal isometric tension testing.
RESULTS: Ribose pre-treatment protected the strength, ductility and toughness of irradiation sterilized bovine and human specimens to differing degrees. Their ultimate strength was not detectably different from non-irradiated control levels; toughness in bovine and human specimens was protected by 57 and 76%, respectively. Untreated human bone was less affected by irradiation and ribose pre-treatment was more effective in human bone than bovine bone.
CONCLUSIONS: This paper presents the first proof-of-principle that irradiation-sterilized bone with improved mechanical properties can be produced through the application of a ribose pre-irradiation treatment, which provides a more stable and connected collagen network than found in conventionally irradiated controls.
METHODS: Experiment 1: The effects of ribose pre-treatment (1.8M in PBS at 60°C for 24h) prior to 33 kGy of irradiation on strength, ductility and toughness (beams in three-point bending) and fracture toughness (J-integral at instability in single edge notched (bending)) were tested against matched non-irradiated and irradiated controls from bovine tibiae. Experiment 2: Three-point bending tests were conducted using beams from human femora (males, 59-67 years). Bone collagen thermal stability and network connectivity were examined using hydrothermal isometric tension testing.
RESULTS: Ribose pre-treatment protected the strength, ductility and toughness of irradiation sterilized bovine and human specimens to differing degrees. Their ultimate strength was not detectably different from non-irradiated control levels; toughness in bovine and human specimens was protected by 57 and 76%, respectively. Untreated human bone was less affected by irradiation and ribose pre-treatment was more effective in human bone than bovine bone.
CONCLUSIONS: This paper presents the first proof-of-principle that irradiation-sterilized bone with improved mechanical properties can be produced through the application of a ribose pre-irradiation treatment, which provides a more stable and connected collagen network than found in conventionally irradiated controls.