Surface engineering: a low wearing solution for metal-on-metal hip surface replacements.

Increased patient blood and serum levels of Co and Cr and dissemination of metal wear particles throughout organs and tissues are the primary concerns with metal-on-metal surface replacements. Surface engineering, providing a ceramic bearing surface on a metal substrate, could provide a solution. This study investigated thick (>10 microm) arc evaporation plasma vapor deposition chromium nitride (CrN) coated surface replacements in terms of wear, ion levels, and wear particles in a 10 million cycle hip simulator study, compared to a contemporary metal-on-metal surface replacement. The ion levels were measured by inductively coupled plasma mass spectroscopy. The wear particles were imaged by field emission gun scanning electron microscopy. The CrN-coated bearings had 80% lower wear than the MoM controls. The Cr and Co ion levels in the lubricant of the CrN bearings were 73 and 98% lower than in the MoM controls. The wear particles produced were in the nanometer size range and round to oval in morphology. The CrN coating could provide a reduction in the wear and ion release of MoM surface replacements, thereby reducing the perceived risks to the patient associated with these prostheses.