Chemically sprayed CdO: Cr thin films for formaldehyde gas detection and optoelectronic applications.

Chromium (Cr) doped CdO films are chemically sprayed and are characterized by their optical, electrical, structural, and microstructural characteristics. The thickness of the films is determined by spectroscopic ellipsometry. The cubic crystal structure with a superior growth along (111) plane of the spray-deposited films is confirmed from the powder X-ray diffraction (XRD) analysis. XRD studies also suggested that some of the Cd2+ ions were substituted by Cr3+ ions, and the solubility of Cr in CdO is minimal, to be around ∼0.75 wt%. The analysis by atomic force microscopy shows uniform distribution of grains throughout the surface, whose roughness is varied from 33 to 13.9 nm concerning Cr-doping concentration. The microstructures from the field emission scanning electron microscope reveal a smooth surface. The elemental composition is examined using an energy dispersive spectroscope. The micro-Raman studies carried out in room temperature endorse the presence of metal oxide (Cd-O) bond vibrations. Transmittance spectra are obtained using UV-vis-NIR spectrophotometer, and the band gap values are estimated from the absorption coefficient. The films show high optical transmittance (>75%) in vis-NIR region. A maximum optical band gap of 2.35 eV is obtained from 1.0 wt% Cr-doping. The electrical measurement (Hall analysis) confirmed the degeneracy nature and n-type semi-conductivity. The carrier density, carrier mobility, and dc-conductivity are increased for higher Cr-dopant percentage. High mobility (85 cm2V-1s-1) is observed for 0.75 wt% Cr-doping. The 0.75 wt% Cr-doping show a remarkable response to formaldehyde gas (74.39%).