Effect of Seed Size on Pervaporation Performances Through FAU Zeolite Membrane.

Pervaporation is a compelling alternative to azeotrope-breaking and solvent dehydration due to lower energy demand and strong selectivity compared with distillation. FAU-type zeolite membranes combine large pore openings and hydrophilic frameworks with robust chemical stability, enabling water-selective separations from alcohols such as isopropanol and ethanol. Despite numerous synthesis routes, the role of seed crystal size in secondary growth, controlling nucleation density, intergrowth, and defect formation remains insufficiently quantified for FAU membranes under identical growth conditions. Here, FAU layers were fabricated on α-Al2O3 supports via secondary growth with varying seed sizes in the nanometer-to-micrometer range (72 nm to 6 μm). Zeolite crystal phase purity and morphology of membranes were assessed by XRD and SEM, with pervaporation of IPA/water 80 wt% at 75 °C quantified flux, separation factor, and permeance. We show that smaller seeds (95.51 nm) increase nucleation density, yielding thinner, more intergrown FAU layers with a higher separation factor but a modest trade-off in flux.