The room temperature ethanol gas sensors based on MoS2-CuGaO2 composite prepared by hydrothermal method.

In this paper, MoS2-CuGaO2 composites were successfully synthesized by hydrothermal method. The composites were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR), X-ray photoelectron spectroscopy (XPS), respectively. The specific surface area and pore size distribution were obtained by N2 adsorption-desorption isotherms. The gas sensing property measurements were conducted. The sensitivity of pure CuGaO2 based gas sensor to 100 ppm acetic acid and benzene vapor was 1.4 at 25oC. The sensitivity of MoS2-CuGaO2 composite (M - 5) was 6.0 towards 100 ppm ethanol vapor at 25oC. And the detection limit of MoS2-CuGaO2 (M - 5) based sensor was 0.1 ppm. The results demonstrated that MoS2 had effect on the selectivity and sensitivity of the MoS2-CuGaO2 composites. M - 5 composite is considered to be promising for ethanol sensing application in room temperature.