Hollow silica-coated porous carbon with embedded iron oxide particles for effective methylene blue degradation.

A novel catalyst, consisting of hollow silica-coated porous carbon with embedded iron oxide particles (FeO x @C/SiO2), was synthesized by the extended Stöber method. Iron ions were incorporated in a resorcinol-formaldehyde resin in the presence of citric acid to form a template, which was then coated with a silica layer. The iron oxide-embedded porous carbon and hollow silica were simultaneously formed during calcination under N2 atmosphere. Through this process, silica endowed the iron oxide with low crystallinity and small size, resulting in a higher catalytic activity in the heterogeneous Fenton system for the decolorization of a methylene blue (MB) solution within 25 min. Moreover, the sample maintained 78.71% of its catalytic activity after three cycles.