Mechanical properties of collagen membranes: are they sufficient for orbital floor reconstructions?

INTRODUCTION

The most common reconstruction materials for orbital floor fractures are PDS (polydioxanone) foil and titanium meshes. These materials have advantages and disadvantages. Therefore, new materials are needed to improve surgical outcomes.

MATERIALS AND

METHODS

Three resorbable collagen membranes (Smartbrane(®), BioGide(®), Creos(®)) were tested for their mechanical properties (puncture strength) in mint and artificially aged (3, 6, 8 weeks) conditions and were compared to PDS foil, titanium meshes (0.25 mm, 0.5 mm) and human orbital floors (n = 7).

RESULTS

The following puncture strengths were evaluated: human orbital floor, 0.81 ± 0.49 N/mm(2); 0.25 mm titanium mesh, 5.36 ± 0.25 N/mm(2); 0.5 mm titanium mesh, 16.08 ± 5.17 N/mm(2); Smartbrane, 0.74 ± 0.31 N/mm(2); BioGide, 1.65 ± 0.45 N/mm(2); and Creos, 2.81 ± 0.27 N/mm(2). After artificial aging, the puncture strengths were significantly reduced (p ≤ 0.05) at 3, 6 and 8 weeks as follows: Smartbrane, 0.05 ± 0.03 N/mm(2), 0.03 ± 0.02 N/mm(2), and 0.01 ± 0.01 N/mm(2), respectively; BioGide, 0.42 ± 0.06 N/mm(2), 0.41 ± 0.12 N/mm(2), and 0.32 ± 0.08 N/mm(2), respectively; and Creos, 2.02 ± 0.37 N/mm(2), 1.49 ± 0.42 N/mm(2), and 1.36 ± 0.42 N/mm(2), respectively.

CONCLUSION

The tested materials showed sufficient puncture strength for orbital floor reconstruction in mint condition. Moreover, after artificial aging, the Creos and BioGide membranes showed sufficient resistance, while Smartbrane showed equivocal data after eight weeks. Therefore, collagen membranes have adequate properties for further in vivo investigations for orbital floor reconstructions.