[Effects of calcium phosphate cement combined with hyaluronic acid/curcumin on the proliferation and osteogenesis of osteoblasts].

OBJECTIVE

After using hyaluronic acid (HA) to modify curcumin (CUR), the effects of calcium phosphate cement (CPC) combined with HA/CUR on the proliferation and osteogenesis of osteoblasts were investigated.

METHODS

First, HA and CUR were esterified and covalently combined to prepare HA/CUR, and the characteristics were observed and the infrared spectrum was tested. Then, HA, CUR, and HA/CUR were mixed with CPC according to 5% ( W/ W) to prepare HA-CPC, CUR-CPC, and HA/CUR-CPC, respectively. Setting time detection, scanning electron microscope observation, injectable performance test, and compression strength test were conducted; and the CPC was used as a control. Osteoblasts were isolated and cultured from the skull of newborn Sprague Dawley rats, and the 2nd generation cells were cultured with the 4 types of bone cement, respectively. The effects of HA/CUR-CPC on the proliferation and osteogenesis of osteoblasts were estimated by the scanning electron microscopy observation, live/dead cell fluorescence staining, cell counting, osteopontin (OPN) immunofluorescence staining, alkaline phosphatase (ALP) staining,and alizarin red staining.

RESULTS

Infrared spectroscopy test showed that HA and CUR successfully covalently combined. The HA/CUR-CPC group had no significant difference in initial setting time, final setting time, injectable rate, and compressive strength when compared with the other 3 groups ( P>0.05); scanning electron microscope observation showed that HA/CUR was scattered on CPC surface. After co-culture of bone cement and osteoblasts, scanning electron microscopy observation showed that the osteoblasts, which had normal morphology and the growth characteristics of osteoblasts, clustered and adhered to HA/CUR-CPC. There was no significant difference in cell survival rate between HA/CUR-CPC group and other groups ( P>0.05), and the number of cells significantly increased ( P<0.05); the degrees of OPN immunofluorescence staining, ALP staining, and alizarin red staining were stronger than other groups.

CONCLUSION

HA/CUR-CPC has good biocompatibility and mechanical properties, which can promote the proliferation and osteogenesis of osteoblasts.