Antimicrobial effect of different physical and chemical compounds of zinc oxide and graphene oxide added to composite resins.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Farhangian Zohre, Alaghehmand Homayoon, Tashakkorian Hamed, Mokhtarpour Faraneh, Davoodabadi Abolfazl
Аннотация
BACKGROUND: Graphene oxide (GO), a product of graphite, is a candidate for nano-reinforcing cement-based materials due to its good water dispersibility and excellent mechanical properties. On the other hand, zinc oxide (ZnO) is well-known for its antibacterial characteristics as well. Therefore, we aimed to evaluate the impacts of adding ZnO and GO nanoparticles on the antibacterial properties of flowable composites.
MATERIALS AND METHODS: In this, in vitro experimental study was designated into five groups containing: (1) no nanoparticles as control group, (2) 1 wt.% ZnO nanoparticle, (3) 1 wt.% GO, (4) 1 wt.% physical compound of ZnO and GO, and (5) 1 wt.% chemical compound of ZnO and GO. The antibacterial properties of composite resin discs were evaluated by direct contact test. Data were analyzed using a one-way analysis of variance, followed by Tukey' post hoc tests (P = 0.05).
RESULTS: Streptococcus mutans colony counting in the first 24 h showed the least growth rate in the chemical compound group (2.2 × 10[5]). However, in 7 days, the least colony number was observed in the GO group (2 × 10[3]). Moreover, the physical compound showed the least bacterial adhesion.
CONCLUSION: Adding GO alone to composites, compared to adding ZnO or physical and chemical compounds of GO-ZnO, was more helpful to increase the antimicrobial characteristics.
MATERIALS AND METHODS: In this, in vitro experimental study was designated into five groups containing: (1) no nanoparticles as control group, (2) 1 wt.% ZnO nanoparticle, (3) 1 wt.% GO, (4) 1 wt.% physical compound of ZnO and GO, and (5) 1 wt.% chemical compound of ZnO and GO. The antibacterial properties of composite resin discs were evaluated by direct contact test. Data were analyzed using a one-way analysis of variance, followed by Tukey' post hoc tests (P = 0.05).
RESULTS: Streptococcus mutans colony counting in the first 24 h showed the least growth rate in the chemical compound group (2.2 × 10[5]). However, in 7 days, the least colony number was observed in the GO group (2 × 10[3]). Moreover, the physical compound showed the least bacterial adhesion.
CONCLUSION: Adding GO alone to composites, compared to adding ZnO or physical and chemical compounds of GO-ZnO, was more helpful to increase the antimicrobial characteristics.