Effect of Impregnation with Natural Shellac Polymer on the Mechanical Properties of Fast-Growing Chinese Fir.

Fast-growing Chinese fir wood has shortfalls such as loose structure and low strength because it grows faster than natural trees. Resin impregnation is a great way to increase the strength of fast-growing fir. However, the resin used for impregnation is a kind of urea-formaldehyde resin, phenolic formaldehyde resin, melamine formaldehyde resin, and the like, which introduce harmful substances such as formaldehyde or phenolic into the wood. In this paper, Chinese fir wood was impregnated with natural shellac polymer, and the effects of impregnation variables on the mechanical properties of the wood were examined. The increase in strength in compression perpendicular to grain (SCPG) of wood samples impregnated with 15% shellac solution achieved a maximum value of 39.01%, but the modulus of rupture (MOR) was slightly reduced. The effects of the impregnation pressure, time, and their interaction were investigated by the response surface method (RSM). ANOVA analysis revealed that the impregnation pressure and time and the interaction between the two seemed to have a significant effect on ∆SCPG. Based on the response face model, the corresponding optimal parameters obtained are 1.0 MPa and 16.0 min for impregnation pressure and time, respectively. By impregnating fir wood with the above optimal conditions, the SCPG increased by 85.78%, whereas the MOR decreased by the least amount.