Biosorption of chromium(VI) and arsenic(V) onto methylated yeast biomass.

Yeast biomass was methylated in a 0.1 M HCl methyl alcohol solution at room temperature and the methylated yeast (MeYE) was applied to the adsorptive separation of Cr(VI) and As(V) anions from aqueous solutions. At near-neutral pH, while Cr(VI) and As(V) anions were scarcely adsorbed onto unmethylated yeast biomass, the amounts adsorbed increased with increasing methylation degree. The amount of Cr(VI) adsorbed onto MeYE was almost constant at pH 4-6 and decreased with increasing pH above pH 6. The amount of As(V) adsorbed onto MeYE was rather lower than that of Cr(VI) and it had a peak at about pH 7. A metal-binding model was used to describe the adsorption characteristics of Cr(VI) and As(V) on MeYE. The results showed that MeYE has two different types of adsorption sites. The saturated amount of Cr(VI) and As(V) adsorbed onto MeYE having methylation degree 0.94 was 0.55 mmol g(-1).