Stabilization of mercury using waste ladle furnace slag.

Disposal of mercury waste has always provided unique challenges due to its high degree of complexity and volatility. This study evaluated the feasibility of using waste LF slag to form a cementitious matrix capable of providing an effective stabilization/solidification solution for the treatment of mercury wastes. The new matrix was synthesized and simulated through a combination of alkali activation and autoclaving process and doped with mercury nitrate at increasing dosage while monitoring the final form of the mercury and its effects on the mineral stability and structure of the new matrix. Compressive strength of up to 20 N/mm2 was achievable for the original matrix. Promising results were obtained in terms of reduced leachability of the mercury when compared to ordinary Portland cement systems at low doping concentration of around 0.5% by weight. A series of precipitation reactions was found to be the main cause responsible for this successful stabilization, especially the metal sulfide precipitation that occurred with the sulfur present in the original waste LF slag.