Novel 3D printable PEEK-HA-Mg2SiO4 composite material for spine implants: biocompatibility and imaging compatibility assessments.
СтатьяПоддержка исследования: вне правительства СШАКомментарийНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Kumar Naresh, Alathur Ramakrishnan Sridharan, Lopez Keith Gerard, Wang Niyou, Vellayappan Balamurugan A, Hallinan James Thomas Patrick Decourcy, Fuh Jerry Ying Hsi, Kumar A Senthil
Аннотация
PURPOSE: To develop a novel 3D printable polyether ether ketone (PEEK)-hydroxyapatite (HA)-magnesium orthosilicate (Mg2SiO4) composite material with enhanced properties for potential use in tumour, osteoporosis and other spinal conditions. We aim to evaluate biocompatibility and imaging compatibility of the material.
METHODS: Materials were prepared in three different compositions, namely composite A: 75 weight % PEEK, 20 weight % HA, 5 weight % Mg2SiO4; composite B: 70 weight% PEEK, 25 weight % HA, 5 weight % Mg2SiO4; and composite C: 65 weight % PEEK, 30 weight % HA, 5 weight % Mg2SiO4. The materials were processed to obtain 3D printable filament. Biomechanical properties were analysed as per ASTM standards and biocompatibility of the novel material was evaluated using indirect and direct cell cytotoxicity tests. Cell viability of the novel material was compared to PEEK and PEEK-HA materials. The novel material was used to 3D print a standard spine cage. Furthermore, the CT and MR imaging compatibility of the novel material cage vs PEEK and PEEK-HA cages were evaluated using a phantom setup.
RESULTS: Composite A resulted in optimal material processing to obtain a 3D printable filament, while composite B and C resulted in non-optimal processing. Composite A enhanced cell viability up to ~ 20% compared to PEEK and PEEK-HA materials. Composite A cage generated minimal/no artefacts on CT and MR imaging and the images were comparable to that of PEEK and PEEK-HA cages.
CONCLUSION: Composite A demonstrated superior bioactivity vs PEEK and PEEK-HA materials and comparable imaging compatibility vs PEEK and PEEK-HA. Therefore, our material displays an excellent potential to manufacture spine implants with enhanced mechanical and bioactive property.
METHODS: Materials were prepared in three different compositions, namely composite A: 75 weight % PEEK, 20 weight % HA, 5 weight % Mg2SiO4; composite B: 70 weight% PEEK, 25 weight % HA, 5 weight % Mg2SiO4; and composite C: 65 weight % PEEK, 30 weight % HA, 5 weight % Mg2SiO4. The materials were processed to obtain 3D printable filament. Biomechanical properties were analysed as per ASTM standards and biocompatibility of the novel material was evaluated using indirect and direct cell cytotoxicity tests. Cell viability of the novel material was compared to PEEK and PEEK-HA materials. The novel material was used to 3D print a standard spine cage. Furthermore, the CT and MR imaging compatibility of the novel material cage vs PEEK and PEEK-HA cages were evaluated using a phantom setup.
RESULTS: Composite A resulted in optimal material processing to obtain a 3D printable filament, while composite B and C resulted in non-optimal processing. Composite A enhanced cell viability up to ~ 20% compared to PEEK and PEEK-HA materials. Composite A cage generated minimal/no artefacts on CT and MR imaging and the images were comparable to that of PEEK and PEEK-HA cages.
CONCLUSION: Composite A demonstrated superior bioactivity vs PEEK and PEEK-HA materials and comparable imaging compatibility vs PEEK and PEEK-HA. Therefore, our material displays an excellent potential to manufacture spine implants with enhanced mechanical and bioactive property.