Mesoporous High-Entropy Alloy Films.

High-entropy alloys (HEAs) are promising materials for electrochemical energy applications due to their excellent catalytic performance and durability. However, the controlled synthesis of HEAs with a well-defined structure and a uniform composition distribution remains a challenge. Herein, a soft template-assisted electrodeposition technique is used to fabricate a mesoporous HEA (m-HEA) film with a uniform composition distribution of Pt, Pd, Rh, Ru, and Cu, providing a suitable platform for investigating structure-performance relationships. Electrochemical deposition enables the uniform nucleation and grain growth of m-HEA, which can be deposited onto many conductive substrates. The m-HEA film exhibits an enhanced mass activity of 4.2 A mgPt-1 toward methanol oxidation reaction (MOR), which is 7.2-fold and 35-fold higher than a mesoporous Pt film and commercial Pt black, respectively. Experimental characterization indicates that structural defects and a low work function of the m-HEA film offer sufficient active sites and fast electron-transfer kinetics. Furthermore, theoretical calculations demonstrate that the variety of favorable adsorption sites on multimetallic elements of HEA reduces the barriers for dehydration pathways and *CO species removal, ensuring optimal performance for complex MOR reactions. This work provides an effective approach to designing a variety of HEA catalysts with well-controlled porous structures for targeted electrocatalytic applications.