Journal of prosthodontic research · 2016
Bond strength of a chairside autopolymerizing reline resin to injection-molded thermoplastic denture base resins.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Hamanaka Ippei, Shimizu Hiroshi, Takahashi Yutaka
Аннотация
PURPOSE: This study evaluated the shear bond strength of a chairside autopolymerizing reline resin to injection-molded thermoplastic denture base resins.
METHODS: Four kinds of injection-molded thermoplastic resins (two polyamides, a polyethylene terephthalate copolymer and a polycarbonate) and PMMA, as a control, were tested. The eight types of surface treatment: ((1) no treatment, (2) air abrasion, (3) dichloromethane, (4) ethyl acetate, (5) 4-META/MMA-TBB resin, (6) air abrasion and 4-META/MMA-TBB resin, (7) tribochemical silica coating, and (8) tribochemical silica coating and 4-META/MMA-TBB resin) were applied to each specimen. The chairside autopolymerizing reline resins were bonded to disks of the injection-molded thermoplastic denture base resins. All of the specimens were immersed in water for 4 months and then thermocycled for 10,000 cycles in water between 5 and 55°C. The shear bond strengths were determined.
RESULTS: The shear bond strengths of the two polyamides treated using air abrasion, dichloromethane and ethyl acetate and no treatment were exceedingly low. The greatest bond strength was recorded for the polyethylene terephthalate copolymer specimens treated with tribochemical silica coating and 4-META/MMA-TBB resin (22.5MPa). The bond strengths of the other injection-molded thermoplastic denture base resins increased using 4-META/MMA-TBB resin.
CONCLUSIONS: Tribochemical silica coating and 4-META/MMA-TBB resin were the most effective surface treatments among all denture base resins tested.
METHODS: Four kinds of injection-molded thermoplastic resins (two polyamides, a polyethylene terephthalate copolymer and a polycarbonate) and PMMA, as a control, were tested. The eight types of surface treatment: ((1) no treatment, (2) air abrasion, (3) dichloromethane, (4) ethyl acetate, (5) 4-META/MMA-TBB resin, (6) air abrasion and 4-META/MMA-TBB resin, (7) tribochemical silica coating, and (8) tribochemical silica coating and 4-META/MMA-TBB resin) were applied to each specimen. The chairside autopolymerizing reline resins were bonded to disks of the injection-molded thermoplastic denture base resins. All of the specimens were immersed in water for 4 months and then thermocycled for 10,000 cycles in water between 5 and 55°C. The shear bond strengths were determined.
RESULTS: The shear bond strengths of the two polyamides treated using air abrasion, dichloromethane and ethyl acetate and no treatment were exceedingly low. The greatest bond strength was recorded for the polyethylene terephthalate copolymer specimens treated with tribochemical silica coating and 4-META/MMA-TBB resin (22.5MPa). The bond strengths of the other injection-molded thermoplastic denture base resins increased using 4-META/MMA-TBB resin.
CONCLUSIONS: Tribochemical silica coating and 4-META/MMA-TBB resin were the most effective surface treatments among all denture base resins tested.