Bond strength of adhesive resin to three nickel-chromium alloys with varying chromium content.

This in vitro study evaluated the influence of chromium content on bond strength and durability between nickel-chromium alloys and an adhesive resin that contained 4-methacryloxyethyl trimellitate anhydride. Three nickel-chromium alloys with different chromium content, as well as pure chromium and pure nickel metals, were bonded and tested for shear strength. After repeated thermocycling, shear bond strength decrease was lower in alloys containing high chromium content. Pure chromium metal demonstrated a 15.2% decrease, whereas pure nickel metal demonstrated the greatest (53.7%) decrease. The results suggest that nickel-chromium alloys with higher chromium content are desirable for 4-methacryloxy-ethyl trimellitate anhydride resin-bonded restorations.