Synthesis and characterisation of microcapsules for self-healing dental resin composites.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Althaqafi Khaled Abid, Satterthwaite Julian, AlShabib Abdulrahman, Silikas Nikolaos
Аннотация
AIM: The purpose of this study was to i) synthesise TEGDMA-DHEPT microcapsules in a laboratory setting; ii) characterise the resultant microcapsules for quality measures.
MATERIALS & METHODS: Microcapsules were prepared by in situ polymerization of PUF shells. Microcapsules characterisation include size analysis, optical and SEM microscopy to measure the diameter and analyse the morphology of PUF microcapsules. FT-IR spectrometer evaluated microcapsules and benzyl peroxide catalyst polymerization independently.
RESULT: Average diameter of TEGDMA-DHEPT microcapsules was 120 ± 45 μm (n: 100). SEM imaging of the capsular shell revealed a smooth outer surface with deposits of PUF nanoparticles that facilitate resin matrix retention to the microcapsules upon composite fracture. FT-IR spectra showed that microcapsules crushed with BPO catalyst had degree of conversion reached to 60.3%.
CONCLUSION: TEGDMA-DHEPT microcapsules were synthesised according to the selected parameters. The synthesised microcapsules have a self-healing potential when embedded into dental resin composite as will be demonstrated in our future work.
MATERIALS & METHODS: Microcapsules were prepared by in situ polymerization of PUF shells. Microcapsules characterisation include size analysis, optical and SEM microscopy to measure the diameter and analyse the morphology of PUF microcapsules. FT-IR spectrometer evaluated microcapsules and benzyl peroxide catalyst polymerization independently.
RESULT: Average diameter of TEGDMA-DHEPT microcapsules was 120 ± 45 μm (n: 100). SEM imaging of the capsular shell revealed a smooth outer surface with deposits of PUF nanoparticles that facilitate resin matrix retention to the microcapsules upon composite fracture. FT-IR spectra showed that microcapsules crushed with BPO catalyst had degree of conversion reached to 60.3%.
CONCLUSION: TEGDMA-DHEPT microcapsules were synthesised according to the selected parameters. The synthesised microcapsules have a self-healing potential when embedded into dental resin composite as will be demonstrated in our future work.