Drug development and industrial pharmacy · 2016
Physicochemical characterization of spray-dried PLGA/PEG microspheres, and preliminary assessment of biological response.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Javiya Curie, Jonnalagadda Sriramakamal
Аннотация
CONTEXT: The use of spray-drying to prepare blended PLGA:PEG microspheres with lower immune detection.
OBJECTIVE: To study physical properties, polymer miscibility and alveolar macrophage response for blended PLGA:PEG microspheres prepared by a laboratory-scale spray-drying process.
METHODS: Microspheres were prepared by spray-drying 0-20% w/w ratios of PLGA 65:35 and PEG 3350 in dichloromethane. Particle size and morphology was studied using scanning electron microscopy. Polymer miscibility and residual solvent levels evaluated by thermal analysis (differential scanning calorimetry - DSC and thermogravimetric analysis - TGA). Immunogenicity was assessed in vitro by response of rat alveolar macrophages (NR8383) by the MTT-based cell viability assay and reactive oxygen species (ROS) detection.
RESULTS: The spray dried particles were spherical, with a size range of about 2-3 µm and a yield of 16-60%. Highest yield was obtained at 1% PEG concentration. Thermal analysis showed a melting peak at 59 °C (enthalpy: 170.61 J/g) and a degradation-onset of 180 °C for PEG 3350. PLGA 65:35 was amorphous, with a Tg of 43 °C. Blended PLGA:PEG microspheres showed a delayed degradation-onset of 280 °C, and PEG enthalpy-loss corresponding to 15% miscibility of PEG in PLGA. NR8383 viability studies and ROS detection upon exposure to these cells suggested that blended PLGA:PEG microspheres containing 1 and 5% PEG are optimal in controling cell proliferation and activation.
CONCLUSION: This research establishes the feasibility of using a spray-drying process to prepare spherical particles (2-3 µm) of molecularly-blended PLGA 65:35 and PEG 3350. A PEG concentration of 1-5% was optimal to maximize process yield, with minimal potential for immune detection.
OBJECTIVE: To study physical properties, polymer miscibility and alveolar macrophage response for blended PLGA:PEG microspheres prepared by a laboratory-scale spray-drying process.
METHODS: Microspheres were prepared by spray-drying 0-20% w/w ratios of PLGA 65:35 and PEG 3350 in dichloromethane. Particle size and morphology was studied using scanning electron microscopy. Polymer miscibility and residual solvent levels evaluated by thermal analysis (differential scanning calorimetry - DSC and thermogravimetric analysis - TGA). Immunogenicity was assessed in vitro by response of rat alveolar macrophages (NR8383) by the MTT-based cell viability assay and reactive oxygen species (ROS) detection.
RESULTS: The spray dried particles were spherical, with a size range of about 2-3 µm and a yield of 16-60%. Highest yield was obtained at 1% PEG concentration. Thermal analysis showed a melting peak at 59 °C (enthalpy: 170.61 J/g) and a degradation-onset of 180 °C for PEG 3350. PLGA 65:35 was amorphous, with a Tg of 43 °C. Blended PLGA:PEG microspheres showed a delayed degradation-onset of 280 °C, and PEG enthalpy-loss corresponding to 15% miscibility of PEG in PLGA. NR8383 viability studies and ROS detection upon exposure to these cells suggested that blended PLGA:PEG microspheres containing 1 and 5% PEG are optimal in controling cell proliferation and activation.
CONCLUSION: This research establishes the feasibility of using a spray-drying process to prepare spherical particles (2-3 µm) of molecularly-blended PLGA 65:35 and PEG 3350. A PEG concentration of 1-5% was optimal to maximize process yield, with minimal potential for immune detection.