Yolk-Shell Encapsulation of Cells by Biomimetic Mineralization and Visible Light-Induced Surface Graft Polymerization.

The pursuit of low-cytotoxicity modification strategies represents a prominent avenue in cell coating research, holding immense significance for the advancement of practical living cell-related technologies. Here, we presented a novel method to fabricate encapsulated yeast cells with a yolk-shell structure by biomimetic mineralization and visible-light-induced surface graft polymerization. In this approach, an amorphous calcium carbonate (ACC) shell was first deposited on the surface of a yeast cell (cell@ACC) modified with 4 layers of self-assembled poly(diallyl dimethylammonium chloride) (PDADMAC)/poly(acrylic acid) (PAA) film using a biomimetic mineralization technique. Subsequently, polyethylenimine (PEI) was absorbed on the surface of cell@ACC by electrostatic interaction. Then, a cross-linked shell was introduced by surface-initiated graft polymerization of poly(ethylene glycol) diacrylate (PEGDA) on cell@ACC under irradiation of visible light using thioxanthone catechol-O,O'-diacetic acid as the photosensitizer. After the removal of the inner ACC shell, the yolk-shell-structured yeast cells (cell@PHS) were obtained. Due to the mild conditions of the strategy, the cell@PHS could retain 98.81% of its original viability. The introduction of the shell layer significantly prolonged the lag phase of yeast cells, which could be tuned between 5 and 25 h by regulating the thickness of the shell. Moreover, the cell@PHS showed improved resistance against lyticase due to the presence of a protective shell. After 30 days of storage, the viability of cell@PHS was 81.09%, which is significantly higher than the 19.89% viability of native yeast cells.