[Study of properties of three-dimensional matrices manufactured by antisolvent 3D printing for reconstruction of extensive bone defects in dentistry and maxillofacial surgery].
Аннотация на английскомСтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Khvorostina M A, Mokrousova V O, Algebraistova P Yu, Nedorubova I A, Kuznetsova V S, Kulakov A A
Аннотация
OBJECTIVE: The aim of the study to study of physical, mechanical and biocompatible properties of the matrices manufactured by antisolvent 3D printing from the solutions of polylactide-co-glycolide in tetraglycol.
MATERIAL AND METHODS: Three-dimensional scaffolds were made from a solution of polylactide-co-glycolide mixed with tetraglycol using antisolvent 3D printing. The elastic properties and the structure of the obtained matrices were studied. MTT-test and staining with PKH-26, Calcein-AM, DAPI with subsequent fluorescence microscopy were used to study biological properties.
RESULTS: The three-dimensional scaffolds had good mechanical properties. Young's modulus value was 18±2 MPa, tensile strength was 0.43±0.05 MPa. The relative survival rate of cells after the first day was 99.58±2.28%, on the 14th day - 98.14±2.22%. The structure of the scaffold promoted cell adhesion and spreading on its surface.
CONCLUSION: The polylactide-co-glycolide matrices produced by antisolvent printing have high porosity, biocompatibility and good mechanical properties. It is allowed to use them in the future as a basis for personalized constructions for the replacement of extensive bone defects of the maxillofacial region.
MATERIAL AND METHODS: Three-dimensional scaffolds were made from a solution of polylactide-co-glycolide mixed with tetraglycol using antisolvent 3D printing. The elastic properties and the structure of the obtained matrices were studied. MTT-test and staining with PKH-26, Calcein-AM, DAPI with subsequent fluorescence microscopy were used to study biological properties.
RESULTS: The three-dimensional scaffolds had good mechanical properties. Young's modulus value was 18±2 MPa, tensile strength was 0.43±0.05 MPa. The relative survival rate of cells after the first day was 99.58±2.28%, on the 14th day - 98.14±2.22%. The structure of the scaffold promoted cell adhesion and spreading on its surface.
CONCLUSION: The polylactide-co-glycolide matrices produced by antisolvent printing have high porosity, biocompatibility and good mechanical properties. It is allowed to use them in the future as a basis for personalized constructions for the replacement of extensive bone defects of the maxillofacial region.