Bioactivity Potential of EndoSequence BC RRM Putty.
СтатьяПоддержка исследования: вне правительства СШАНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Moinzadeh Amir T, Aznar Portoles Carlos, Schembri Wismayer Pierre, Camilleri Josette
Аннотация
INTRODUCTION: The aim of this study was to characterize and assess the interaction of EndoSequence BC RRM putty (Brasseler USA, Savannah, GA) in contact with blood and simulated body fluid. Tricalcium silicate-based materials are in contact with blood and tissue fluids during and after their setting. These materials are hydraulic; thus, their properties improve in moist conditions. However, specific environmental conditions may modify the material setting.
METHODS: EndoSequence BC RRM putty was characterized by scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction analysis. This was done before setting and after contact with water, Hank's balanced salt solution, and heparinized whole blood. Furthermore, characterization of an explanted material from a failed root-end surgery was performed.
RESULTS: The EndoSequence BC RRM putty was composed of tricalcium silicate, tantalum oxide, and zirconium oxide. The tricalcium silicate reaction led to the formation of calcium hydroxide, and this was evident over the putty in contact with water and Hank's balanced salt solution. In the latter case, there was also the formation of globular crystals synonymous with hydroxyapatite formation. The material in contact with blood exhibited a poorly crystalline surface with additional peaks for calcium, phosphorus, and chlorine, whereas the material retrieved from the failed root-end surgery had deposition of calcium carbonate on its surface.
CONCLUSIONS: The environmental conditions affect the hydration of the EndoSequence RMM putty and consequentially the material interaction with the environment. However, in vitro material assessment may not be representative of the clinical situation because carbon dioxide present in vivo leads to the formation of calcium carbonate rather than the hydroxyapatite reported in in vitro studies.
METHODS: EndoSequence BC RRM putty was characterized by scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction analysis. This was done before setting and after contact with water, Hank's balanced salt solution, and heparinized whole blood. Furthermore, characterization of an explanted material from a failed root-end surgery was performed.
RESULTS: The EndoSequence BC RRM putty was composed of tricalcium silicate, tantalum oxide, and zirconium oxide. The tricalcium silicate reaction led to the formation of calcium hydroxide, and this was evident over the putty in contact with water and Hank's balanced salt solution. In the latter case, there was also the formation of globular crystals synonymous with hydroxyapatite formation. The material in contact with blood exhibited a poorly crystalline surface with additional peaks for calcium, phosphorus, and chlorine, whereas the material retrieved from the failed root-end surgery had deposition of calcium carbonate on its surface.
CONCLUSIONS: The environmental conditions affect the hydration of the EndoSequence RMM putty and consequentially the material interaction with the environment. However, in vitro material assessment may not be representative of the clinical situation because carbon dioxide present in vivo leads to the formation of calcium carbonate rather than the hydroxyapatite reported in in vitro studies.