Double-Crown Prosthesis Retention Using Polyetherketoneketone (PEKK): An In Vitro Study.
СтатьяНазвание и аннотация: Перевод в очереди
Обработка статьи · этапы, ошибки и управление
Загрузка состояния…
Ошибки и ограничения
История · было → стало
Состояние обновляется каждые 5 секунд, пока блок открыт. Процент показывается только там, где известен объём работы. Пауза останавливает продолжение этапа; текущий запрос к источнику может завершиться.
Igarashi Kensuke, Katagiri Hiroki, Abou-Ayash Samir, Schimmel Martin, Afrashtehfar Kelvin I
Аннотация
PURPOSE: To assess the retentive force of telescopic crowns using polyetherketoneketone (PEKK) high-performance polymer in relation to conventional materials over a long period of time in an in vitro setting.
MATERIALS AND METHODS: Thirty-six sets of primary and secondary crowns were fabricated as per the double crown-retained prostheses approach. Six samples were included in each of the five test groups (1: zirconia/PEKK [Zr/PEKK]; 2: titanium/PEKK [Ti/PEKK]; 3: cobalt-chrome/PEKK [CoCr/PEKK]; 4: PEKK/PEKK; and 5: gold/PEKK [Au/PEKK]) and the single control group (gold/galvano-gold [Au/GA]). The insertion-removal test was performed for 20,000 cycles, and the surface condition was observed. Retentive forces were analyzed using two-way ANOVA (α<0.05).
RESULTS: The retention forces in groups Zr/PEKK and Ti/PEKK significantly decreased over time (group 1: p = 0.035 and group 2: p = 0.001), whereas retentive force increased significantly in groups PEKK/PEKK, Au/PEKK, and control (group 4: p = 0.001, group 5: p = 0.008, and control: p = 0.042). Similar wear was observed on the primary crown in groups PEKK/PEKK, gold/PEKK, and control.
CONCLUSIONS: Groups PEKK/PEKK and Au/PEKK showed a transition of retentive force similar to the control group. Groups PEKK/PEKK and Au/PEKK had similar wear on the surface compared to control. Therefore, PEKK has a promising clinical potential.
MATERIALS AND METHODS: Thirty-six sets of primary and secondary crowns were fabricated as per the double crown-retained prostheses approach. Six samples were included in each of the five test groups (1: zirconia/PEKK [Zr/PEKK]; 2: titanium/PEKK [Ti/PEKK]; 3: cobalt-chrome/PEKK [CoCr/PEKK]; 4: PEKK/PEKK; and 5: gold/PEKK [Au/PEKK]) and the single control group (gold/galvano-gold [Au/GA]). The insertion-removal test was performed for 20,000 cycles, and the surface condition was observed. Retentive forces were analyzed using two-way ANOVA (α<0.05).
RESULTS: The retention forces in groups Zr/PEKK and Ti/PEKK significantly decreased over time (group 1: p = 0.035 and group 2: p = 0.001), whereas retentive force increased significantly in groups PEKK/PEKK, Au/PEKK, and control (group 4: p = 0.001, group 5: p = 0.008, and control: p = 0.042). Similar wear was observed on the primary crown in groups PEKK/PEKK, gold/PEKK, and control.
CONCLUSIONS: Groups PEKK/PEKK and Au/PEKK showed a transition of retentive force similar to the control group. Groups PEKK/PEKK and Au/PEKK had similar wear on the surface compared to control. Therefore, PEKK has a promising clinical potential.