Methanol-induced assembly and pyrolysis preparation of three-dimensional N-doped interconnected open carbon cages supported FeNb2O6 nanoparticles for boosting oxygen reduction reaction and Zn-air battery.

Three-dimensional (3D) hollow carbon is one of advanced nanomaterials widely applied in oxygen reduction reaction (ORR). Herein, iron niobate (FeNb2O6) nanoparticles supported on metal-organic frameworks (MOFs)-derived 3D N-doped interconnected open carbon cages (FeNb2O6/NICC) were prepared by methanol induced assembly and pyrolysis strategy. During the fabrication process, the evaporation of methanol promoted the assembly and cross linkage of ZIF-8, rather than individual particles. The assembled ZIF-8 particles worked as in-situ sacrificial templates, in turn forming hierarchically interconnected open carbon cages after high-temperature pyrolysis. The as-made FeNb2O6/NICC showed a positive onset potential of 1.09 V and a half-wave potential of 0.88 V for the ORR, outperforming commercial Pt/C under the identical conditions. Later on, the as-built Zn-air battery with the FeNb2O6/NICC presented a greater power density of 100.6 mW cm-2 and durable long-cycle stability by operating for 200 h. For preparing 3D hollow carbon materials, this synthesis does not require a tedious removal process of template, which is more convenient than traditional method with silica and polystyrene spheres as templates. This work affords an exceptional example of developing 3D N-doped interconnected hollow carbon composites for energy conversion and storage devices.