Nanoconfinement-Driven Energy-Efficient CO2 Capture and Release at High Pressures on a Unique Large-Pore Mesoporous Carbon.

Although microporous carbons can perform well for CO2 separations under high pressure conditions, their energy-demanding regeneration may render them a less attractive material option. Here, we developed a large-pore mesoporous carbon with pore sizes centered around 20-30 nm using a templated technical lignin. During the soft-templating process, unique cylindrical supramolecular assemblies form from the copolymer template. This peculiar nanostructuring takes place due to the presence of polyethylene glycol (PEG) segments on both the Pluronic® template and the PEG-grafted lignin derivative (glycol lignin). A large increase in CO2 uptake occurs on the resulting large-pore mesoporous carbon at 270 K close to the saturation pressure (3.2 MPa), owing to capillary condensation. This phenomenon enables a CO2/CH4 selectivity (SCO2/CH4, mol/mol) of 3.7 at 270 K and 3.1 MPa absolute pressure, and a swift pressure swing regeneration process with desorbed CO2 per unit pressure far outperforming a benchmark activated carbon (i.e., notably rapid decrease in the amount of adsorbed CO2 with decreasing pressure). We propose large-pore mesoporous carbons as a novel family of CO2 capture adsorbents, based on the phase-transition behavior shift of CO2 in the nanoconfined environment. This novel material concept may open new horizons for physisorptive CO2 separations with energy-efficient regeneration options.