Vanadium Phosphorus Oxide/Siliceous Mesostructured Cellular Foams: efficient and selective for sustainable acrylic acid production via condensation route.

A new type of supported vanadium phosphorus oxide (VPO) with self-phase regulation was simply fabricated (organic solvent free) for the first time by depositing the specific VPO precursor NH4(VO2)HPO4 onto the Siliceous Mesostructured Cellular Foams (MCF) with controlled activation. The resulting materials were found to be highly efficient and selective for sustainable acrylic acid (AA) plus methyl acrylate (MA) production via a condensation route between acetic acid (HAc) and formaldehyde (HCHO). A (AA + MA) yield of 83.7% (HCHO input-based) or a (AA + MA) selectivity of 81.7% (converted HAc-based) are achievable at 360 °C. The systematic characterizations and evaluations demonstrate a unique surface regulation occurring between the MCF and the NH4(VO2)HPO4 precursor. NH3 release upon activation of NH4(VO2)HPO4 precursor together with adsorption of NH3 by MCF automatically induces partial reduction of V5+ whose content is fine-tunable by the VPO loading. Such a functionalization simultaneously modifies phase constitution and surface acidity/basicity of catalyst, hence readily controls catalytic performance.